SciELO - Scientific Electronic Library Online

 
vol.88 issue216Bibliometric analysis of engineering publications in Colombia 2010-2019: a Scopus analysisA case study on causation of the landslide on 26 October 2016 in the northern Colombian Andes author indexsubject indexarticles search
Home Pagealphabetic serial listing  

Services on Demand

Journal

Article

Indicators

Related links

  • On index processCited by Google
  • Have no similar articlesSimilars in SciELO
  • On index processSimilars in Google

Share


DYNA

Print version ISSN 0012-7353On-line version ISSN 2346-2183

Dyna rev.fac.nac.minas vol.88 no.216 Medellín Jan./Mar. 2021  Epub May 24, 2021

https://doi.org/10.15446/dyna.v88n216.88247 

Articles

Identification and analysis of pathological defect appearance in superstructures of reinforced-concrete bridges in Chapare region, Bolivia

Identificación y análisis de las manifestaciones patológicas en la superestructura de puentes de concreto armado en la región de Chapare, Bolivia

Joaquin Humberto Aquino Rochaa 

Rolando Ibarra-Villanuevab 

a Facultad de Tecnología, Universidad Privada del Valle, Cochabamba, Bolivia. jaquinor@univalle.edu

b Empresa Nacional de Electricidad, Cochabamba, Bolivia. rolando.ibarra1@gmail.com


Abstract

The objective of this article is to identify and analyze the main pathological manifestations in bridges in the Chapare - Bolivia region, an area characterized by high humidity and constant rainfall throughout the year. The methodology consisted of the selection of five bridges that showed evident signs of deterioration, in which a visual inspection was carried out and, subsequently, different tests: sclerometer, carbonation depth, penetration of chlorides and core extraction. All the bridges present advanced states of deterioration; highlighting corrosion as the main problem, generating detachment of the concrete and risk of collapse. Although the concrete has a compression strength greater than 30 MPa, the existing carbonation process and the different problems encountered compromises it. It is necessary that the entities in charge provide inspection and maintenance programs according to the environmental and structural characteristics of each bridge.

Keywords: inspection; sclerometer; carbonation depth; core extraction

Resumen

El objetivo del presente artículo es identificar y analizar las principales manifestaciones patológicas en puentes de la región de Chapare - Bolivia, zona caracterizada por elevada humedad y constantes lluvias durante todo el año. La metodología consistió en la selección de cinco puentes que presentaban señales evidentes de deterioro, en los cuales se realizó una inspección visual y, posteriormente, diferentes ensayos: esclerómetro, profundidad de carbonatación, penetración de cloruros y extracción de núcleos. Los resultados muestran que todos los puentes presentan estados avanzados de deterioro; destacándose la corrosión como el principal problema, generando desprendimiento del hormigón y riesgo de colapso. Si bien el hormigón tiene resistencia a la comprensión mayor a 30 MPa, este se encuentra comprometido por el proceso de carbonatación existente y los diferentes problemas encontrados. Es necesario que las entidades encargadas provean programas de inspección y mantenimiento de acuerdo con las características ambientales y estructurales de cada puente.

Palabras clave: inspección; esclerómetro; profundidad de carbonatación; extracción de núcleos

1. Introduction

Bridges are important structures for economic and social development of communities and become the civil infrastructure of a country to support communication between points including any kind of barriers [1]. There are many design criteria for these structures in order to obtain safety, reliability and durability. However, bridges are prone to develop certain pathological defects due to different aspects: aggressive environment, chemical attacks, more than expected intense traffic, and low quality material, among others, which causes a fast deterioration of their structure. Accordingly, inspection and maintenance activities to preserve and extend useful life of these structures are required [2-4].

Bridge inspection is not a regulated activity in Bolivia. This is the reason why it is not performed in most cases, unlike other countries where specific standards are enforced. In Europe, for example, routine inspections are performed on a yearly basis and detailed inspections are performed as required or according to inspector advice, every five years [5]. In Brazil, an inspection must be performed every year and detailed inspections every five to eight years [6]. In the United States, inspection frequency is every two years [7,8]. Despite this, however, 23% of structures are deficient or operationally obsolete [9]; it is reported that useful life of a bridge in the United States is 42 years, even when they have been designed and built to be used during 50 years [10].

Among main pathological defects found during bridge inspection, iron corrosion, fissures, fungus, and efflorescence, among others [3,11]. Being corrosion the most common and costly issue for intervention and maintenance activities [12].

Usually, bridge inspection is visual and performed by certified inspectors who assess different elements [2]. Even so, this approach involves some inconveniences such as lack of reliability and high variability of results, which are mostly based on each inspector’s experience [13,14]. Therefore, including different tests is required in order to give a more precise diagnosis. Core extraction is a destructive test to determine resistance to concrete compression, traction and flexion in existing structures [15], as well as finding internal defects [16]. Combined with non-destructive tests, results are trustworthy [17]. Despite specific information that could be provided by this essay, it is limited to small volumes of concrete.

Non-destructive testing poses different advantages for inspection processes such as promptness and effectiveness. Available literature presents advantages and limitations, as well as guidelines to be used during inspection and evaluation of structures. These include: Ground Penetrating Radar [2], Impact-Echo [18], electrical resistivity [19], infrared thermography [20,21], carbonation depth by phenolphthalein spraying [3], and chloride penetration [22], among others. Nevertheless, there is a wide variety including different physical principles [14,24].

This article is intended to apply different destructive and non-destructive testing methods to analyze pathological defect appearance in superstructures of five bridges located in Chapare-Bolivia region, since they show evident issues and no inspection or maintenance programs are available in the area. Tests used included sclerometer, carbonation depth and chloride penetration in order to verify results with core extraction.

2. Methodology

Five bridges on the Cochabamba-Santa Cruz Road (RN4), located in Chapare region in Bolivia were selected (Fig. 1). This road is part of the national route and has been used for 51 years since it was built.

Source: Adapted from [25].

Figure 1 Location of selected bridges. 

2.1 Selected bridges

  • a) Málaga Bridge: It is located in chainage 85+650 (RN4), canted by 10%, and including a slope of 4.58%.

  • This bridge does not show deviation but certain developing curvature with 82.56-meter radius and consists of three sections, each 21.60 m long, resulting in a total length of 64.80 m.

  • b) Ronco Bridge: It is located in chainage 90+950 (RN4), canted by 10% and including a slope of 6.97%.

  • This bridge shows a deviation of 13º and its developing curvature is 79.58-meter radius. It includes a single section 21.60 m long.

  • c) Ronquito Bridge: It is located in chainage 91+125 (RN4), canted by 10% and including a slope of 0.30%. This bridge shows a developing curvature including 102.31-meter radius and a single section 21.00 m long.

  • d) Roquemayu Bridge: It is located in chainage 98+100 (RN4), canted by 10% and including a slope of 1.35%. This bridge does not show any deviation, but its developing curvature includes 119.37-meter radius and a single section 21.00 m long.

  • e) San Jacinto Bridge: It is located in chainage 99+550 (RN4), canted by 7% and including a slope of 2.30%. This bridge includes three sections 22.70, 23.00 and 22.70 m long, respectively, with a total length of 68.40 m.

2.2 Characterization of the study area

The study area, Chapare Region in Bolivia, is located in a subtropical area, characterized by high relative humidity and constant rainfall, 3801 mm per year. Average annual temperature is 25.2°C [26]. Fig. 2 summarizes historical data for rainfall and temperature in the region during 1982-2012 period.

Source: Adapted from [26].

Figure 2 Historical data for weather in the study area. 

2.3 Preliminary and detailed inspection

Initially, a preliminary inspection consisting in a visual test identifying the main characteristics for place, weather and relative humidity, visible issues and specific location for every bridge, its access and ability to perform testing was performed.

Subsequently, a more detailed inspection, surveying the total of pathological defect appearance, using a checklist and photographs was performed. Then, non-destructive (silver nitrate spraying, phenolphthalein spraying and sclerometer) testing and destructive (core extraction) testing were implemented for a better characterization of pathological defects found. Procedure adopted for each essay is described below:

  • a) Colorimetric method by silver nitrate spraying:

  • UNI 7928 Italian Standard [27] was considered. This standard establishes silver nitrate solution with a concentration of 0.1 mol/l, this is 17 g of AgNO3 per 1 liter of distilled water. During inspection, cracks in small areas of the concrete structure were found, where then a solution of silver nitrate was sprayed. This area remained in a lightened environment (sun exposure) so that photochemical reaction between the solution and the concrete surface took place. Afterwards, a photographic record for the visual analysis of surface coloring was performed. Three points per bridge were determined.

  • a) Colorimetric method by phenolphthalein spraying:

  • In order to perform this test, CPC-18 RILEM Standard [28] was considered. This standard establishes a solution of 1g phenolphthalein dissolved in 100 g of 70% ethylic alcohol. After being prepared, phenolphthalein solution was stored in a recipient for further use. During inspection, cracks in small areas of concrete structure were made with a hammer drill and phenolphthalein solution was then sprayed. Subsequently, a photographic record for a visual analysis of surface coloring was performed. This allowed measurement of carbonation depth. Three points per bridge were registered. It is worth mentioning that this test was performed on extracted cores.

  • b) Sclerometer Testing: In order to perform this test, 7584 NBR Standard [29], which guidelines an appropriate performance, was considered. In order to start the test, assessed areas where dried and polished with a prism to obtain a smooth finish on the surface. A PROCEQ Original Schmidt N hammer was used. A total of 8 tests per bridge were registered.

  • c) Core extraction: C42/C42M-04 Standard [15] was considered. This standard provided guidelines to obtain, prepare and test cores extracted from concrete in order to determine compression resistance, a value that is to be analyzed in this investigation. Cores were 10 cm in diameter (D) and 20 cm long (L) with corrections whenever L/D ratio was less than 1.75. Two cores per bridge were extracted in points where sclerometer testing had been previously performed.

Fig. 3 shows in detail the tests performed in all five bridges studied.

Source: The authors.

Figure 3 Location of tests performed. 

3. Analysis and discussion of results

3.1 Pathological appearances

During visual inspection, fissures and concrete disaggregation exposing armatures were found in every case. Latter issue is due to steel corrosion process, which gradually evidenced reinforcement exposure with oxidation and loss of cross section (Fig. 4). In addition, it was also evidenced that in some cases it was produced by a motor vehicle accident on the bridge (Fig. 5).

Source: The authors.

Figure 4 Disaggregation of concrete and armatures exposed: a) San Jacinto and b) Ronco bridges. 

Source: The authors.

Figure 5 Structures impacted by accidents: a) Roquemayu and b) Ronquito bridges. 

Another pathological defect found was excessive vegetation, fungus and moss due to high relative humidity in the air and constant rainfall in the region. These issues are shown in Fig. 6.

Source: The authors.

Figure 6 Vegetation, fungus and moss: a) Ronco, b) Ronquito, c) Roquemayu, and d) San Jacinto bridges. 

It was observed that 100% of the bridges show every issue considered, except for Málaga Bridge, which does not present vegetation (plants) in its superstructure.

Additionally, during inspection it could be verified that some bridges present their drainage systems obstructed by garbage or vegetation, thus evidencing lack of cleaning service (Fig. 7).

Source: The authors.

Figure 7 Obstructed drainage: a) Ronquito and b) Ronco bridges. 

3.2 Carbonation depth

Even though corrosion was evidenced in very bridge through concrete disaggregation, additionally, three carbonation depth tests (C1-C2-C3) with colorimetric method by phenolphthalein were performed on every bridge. Table 1 presents results of testing performed.

Table 1 Results for carbonation depth testing 

*Corrosion detected in iron

Source: The authors.

When concrete was broken in some points, iron corrosion was observed. This was verified by carbonation depth testing, since concrete coating showed no coloring compared to concrete found in inner layers (Fig. 8). It is important to mention that every bridge showed advanced carbonation, which reveals decrease in concrete alkalinity, hydrogen potential (pH) values below eight, which generates iron depassivation [30], that produces corrosion in bars evaluated, although points where carbonation depth was zero, showed corrosion is not present in the whole bridge, but only in some areas.

Source: The authors.

Figure 8 Carbonation Depth: a) Roquemayu Bridge and b) Málaga Bridge. 

This corrosion process is due to carbon dioxide (CO2) present in the environment and high relative humidity in this region, as dry pores show no CO2 in progress in concrete due to lack of water. Otherwise, whenever the pores are full of water, carbonation process has ideal conditions to progress until reaching the iron [12]. Additionally, temperature is high in the area, which favors progressive corrosion [31].

3.3 Chloride penetration

When applying a colorimetric method by silver nitrate spraying no results were found in any of three points tested per bridge (P1-P2-P3), which was expected, because chloride penetration is mainly present in marine environments [32,33], and this method does not generate any results when pH is below ten [34]. As shown in previous section, corrosion process by carbonation is present in every bridge.

3.4 Surface hardness rate

Table 2 shows results for surface hardness rate per bridge. Málaga Bridge has the highest average, 48.6, and the least dispersion data, standard deviation of 2.1. Ronquito Bridge showed a lower average, 38, and a significant dispersion, standard deviation of 3.2. Nevertheless, the greatest dispersion regarding average results involved Roquemayu Bridge with a value of 5.3.

Table 2 Results for Surface Hardness Rate. 

Source: The authors.

Fig. 9 shows a box-and-whisker plot of results for surface hardness per bridge. It is evident that every bridge, except for Ronco Bridge, present a negative asymmetry, the average is below the median, which shows data concentrate on the upper part of distribution. In the case of Ronco Bridge, data concentrate in the lower part.

Source: The authors.

Figure 9 Box-and-whisker plot of results for surface hardness rate per bridge. 

Málaga Bridge shows that 50% data ranges between 46.5 and 50.3 of surface hardness rate, an interquartile range of 3.8 showing that ranges are close, and value dispersion is low when compared against graphics for other bridges. In contrast, Roquemayu presents the highest interquartile range, 3.8, thus showing a wide value dispersion for surface hardness rate.

It is important to consider that sclerometer test results are influenced by concrete age and carbonation [35,36]. As previously mentioned, studied bridges are old and present carbonation in some areas, thus generating variability in results. However, rate values for surface hardness are used to compare dispersion among these bridges. It was noticed that concrete in Málaga Bridge is better qualified than concrete found in Ronquito Bridge and that concrete in Roquemayu Bridge is the most heterogeneous.

3.5 Core extraction

Table 3 shows results for core extraction, compression resistance and carbonation depth. Additionally, resistance values were added to estimated compression according to surface hardness rate for points E1 and E8. Even though resistance estimation through models reported in literature, -including the manufacturers-, is not completely reliable [23], in this case, they will only be used to be compared against values obtained. It is worth mentioning that estimated values for compression resistance were corrected for carbonation depth, following manufacturer’s recommendations [36].

Table 3 Results for core extraction. 

*NCT - No compression test was performed due to iron present in the core

Source: The authors.

Compression resistance is high in cores, greater than 30 MPa. These values are appropriate and recommended for this type of structure [37], but carbonation presence is evident in almost every extracted core.

Fig. 10 shows both core extraction and compression testing. In the case of N2-E8 for Roquemayu Bridge, compression test was performed according to C42/C42M-04 recommendations [15]. This core presented iron and oxidation products (Fig. 11).

Source: The authors.

Figure 10 a) Core extraction, and b) Compression Test - Ronquito Bridge 

Figure 11 Roquemayu Bridge core presenting oxidation products. 

A correlation between compression resistance in cores and sclerometer testing was made as shown in Fig. 12. A high positive linear relation could be observed (R 2 =0.695). Nevertheless, significance of correlation coefficient must be determined.

Source: The authors.

Figure 12 Correlation between compression resistance in cores and sclerometer testing. 

Significance refers to the probability that this correlation coefficient (R) comes from a population whose coefficient has value zero. This is why two hypothesis are posed: 1) H0:R=0, calculated correlation coefficient comes from a population whose correlation coefficient is zero, and 2) H1:R=0, calculated correlation coefficient comes from a population whose correlation coefficient is other than zero.

A t-student test with eq. (1) is applied.

Where: N, data number, 9 in this case, considering that point N2-E8 was not included in the correlation. Value calculated for t is 3.99.

Value tα,N-2=2.36 is obtained in t-student distribution tables for α=0.05. Then: t > tα,N-2, therefore null hypothesis (H0) with an error probability of 0.05 is rejected. Obtained correlation does not come from a population characterized for having zero correlation. There is a relation between compression resistance both in core and sclerometer testing.

Even though a relation between compression resistance in cores and sclerometer testing is present due to results obtained, determination coefficient (R 2 ) is lower when compared against results found in literature [23]. This is mainly due to data amount. For current investigation, cores were extracted in 10 points only, from which only 9 could be correlated. A greater number of data will enable making different correlations and proposing different models for better adjustment.

Concrete in bridges is acceptable in terms of compression resistance, but corrosive processes that produce disaggregation and armature exposition compromise it. For this issue, different techniques for structural recovery could be implemented, but corrosion process is advanced, and risk of collapse is present. Intervention or structures replacement should be implemented once they serve their useful life [30].

This study has been limited to four tests and an inspection to bridge superstructures, due to difficult access to other areas, and rushing rivers in this region. For a better characterization of defaults and a global study, other non-destructive tests cited in literature may be implemented [14,39], and even an Unmanned Aerial Vehicle (UAV) [40] could be used in difficult access areas such as bridge infrastructure.

4. Final considerations

Bridges in this study show no maintenance service, and they are highly deteriorated. Humidity is a common factor that causes appearance of different issues such as fungus, vegetation and moss, as they also favor corrosive process.

Many corroded portions were detected in the bridges, mainly developed by carbonation. This process could not enable chloride detection.

Non-destructive tests applied generate qualitative and disperse values, but allow comparison and characterization of pathological issues, thus complementing preliminary (visual) inspection. This way, a more accurate diagnosis about structure status is possible.

A model that relates compression resistance in both core and sclerometer testing was found. Although limited, it generates a starting point for further studies in these structures.

Results must be considered by institutions in charge of providing regular inspection and maintenance programs. This way, a proper performance of these structures, mainly in areas where environmental conditions favor a rapid concrete deterioration, may be guaranteed.

References

[1] Mascia, N.T. and Sartorti, A.L., Identification and analysis of pathologies in bridges of urban and rural roads. Revista Ingeniería de Construcción, 26(1), pp. 5-24, 2011. DOI: 10.4067/S0718-50732011000100001 [ Links ]

[2] Dabous, S. and Feroz, S., Condition monitoring of bridges with non-contact testing technologies. Automation in Construction, 116, pp. 103224, 2020. DOI: 10.1016/j.autcon.2020.103224 [ Links ]

[3] Esteves, I.C.A., Medeiros-Junior, R.A. and Medeiros, M.H.F., NDT for bridges durability assessment on urban-industrial environment in Brazil. International Journal of Building Pathology and Adaptation, 36(5), pp. 500-515, 2018. DOI: 10.1108/ijbpa-04-2018-0032 [ Links ]

[4] Rocha, J.H.A. and Póvoas, Y.V., Detección de delaminaciones en puentes de concreto armado usando Termografía Infrarroja. Revista Ingeniería de Construcción, 34(1), pp. 55-64, 2019. DOI: 10.4067/S0718-50732019000100055 [ Links ]

[5] Everett, T.D., Weykamp, P., Capers H.A., Cox, R.W., Drda, T.S., Hummel, L., Jensen, P., Juntunen, D.A., Kimball, T. and Washer, G.A., Bridge Evaluation Quality Assurance in Europe. FHWA-HPIP, Washington D.C., United States, 2008. 56 P. [ Links ]

[6] Associação Brasileira de Normas Técnicas - ABNT. NBR 9452: Inspeção de pontes, viadutos e passarelas de concreto - Procedimento. ABNT, Rio de Janeiro, Brasil, 2016. [ Links ]

[7] Pines, D. and Aktan, A.E., Status of structural health monitoring of long-span bridges in the United States. Progress in Structural Engineering and Materials, 4(4), pp. 372-380, 2002. DOI: 10.1002/pse.129 [ Links ]

[8] Electronic Code of Federal Regulations. Subpart C, Title 23, 650.311, [online]. Washington, D.C., USA, 2016. Available at: https://www.ecfr.gov/cgi-bin/text-idx?SID=a4fdd8389550f9ece2bee1b5ecc0e822&mc=true&node=se23.1.650_1311&rgn=div8Links ]

[9] United States Department of Transportation - USDT. Chapter 2: growth, deregulation, and intermodalism. [online]. Washington D.C., USA, 2017. Available at: https://www.bts.gov/archive/publications/the_changing_face_of_transportation/chapter_02Links ]

[10] Herrmann, A.W., ASCE 2013 Report card for America’s Infrastructure. IABSE Symposium Report, International Association for Bridge and Structural Engineering, 2013, pp. 9-10. [ Links ]

[11] Lima, H.J.N., Ribeiro, R.S., Palhares, R.A. y Melo, G.S.S.A., Análisis de manifestaciones patológicas del concreto en viaductos urbanos, Revista ALCONPAT, 9(2), pp. 247-259, 2019. DOI: 10.21041/ra.v9i2.308 [ Links ]

[12] Meira, G.R., Corrosão de armaduras em estruturas de concreto: fundamentos, diagnóstico e prevenção. Brasil, João Pessoa: IFPB, 2017. [ Links ]

[13] Phares, B.M., Washer, G.A., Rolander, D.D., Graybeal, B.A. and Moore, M., Routine highway bridge inspection condition documentation accuracy and reliability. Journal of Bridge Engineering, 9(4), pp. 403-413, 2004. DOI: 10.1061/(ASCE)1084-0702(2004)9:4(403) [ Links ]

[14] Rehman, S., Ibrahim, Z., Memon, S. and Jameel, M., Nondestructive test methods for concrete bridges: a review. Construction and Building Materials, 107(15), p. 58-86, 2016. DOI: 10.1016/j.conbuildmat.2015.12.011 [ Links ]

[15] American Standards for Testing Materials - ASTM. C 42/C42M-04: Standard test method for obtaining and testing drilled cores and sawed beams of concrete, West Conshohocken: ASTM, Pensilvania, United States, 2004. [ Links ]

[16] Oh, T., Kee, S., Arndt, R., Popovics, J. and Zhu, J., Comparison of NDT Methods for Assessment of a Concrete Bridge Deck. Journal of Engineering Mechanics, 193(3), pp. 305-314, 2013. DOI: 10.1061/(ASCE)EM.1943-7889.0000441 [ Links ]

[17] Scott, M., Rezaizadeh, A., Delahaza, A., Santos, C., Moore, M., Graybeal, B. and Washer, G., A comparison of nondestructive evaluation methods for bridge deck assessment. NDT & E International, 36(4), pp. 245-255, 2003. DOI: 10.1016/s0963-8695(02)00061-0 [ Links ]

[18] Azari, H. and Lin, S., Evaluation of the impact echo method for concrete bridge decks with asphalt overlays. Transportation Research Record, 2673(2), pp. 436-444, 2019. DOI: 10.1177/0361198119828676 [ Links ]

[19] Karim, M.Z., Tucker-Kulesza, S.E. and Bernhardt-Barry, M., Electrical resistivity as a binary classifier for bridge scour evaluation. Transportation Geotechnics, 19, pp. 146-157, 2019. DOI: 10.1016/j.trgeo.2019.03.002 [ Links ]

[20] Omar, T., Nehdi, M.L. and Zayed, T., Infrared thermography model for automated detection of delamination in RC bridge decks. Construction and Building Materials, 168, pp. 313-327, 2018. DOI: 10.1016/j.conbuildmat.2018.02.126 [ Links ]

[21] Hiasa, S., Birgul, R., Matsumoto, M. and Necati-Catbas, F., Experimental and numerical studies for suitable infrared thermography implementation on concrete bridge decks. Measurement, 121, pp. 144-159, 2018. DOI: 10.1016/j.measurement.2018.02.019 [ Links ]

[22] Real, L.V., Oliveira, D.R.B., Soares, T. y Medeiros, M.H.F., Método colorimétrico por aspersión de nitrato de plata para la evaluación de la penetración de cloruros en concreto: estado del arte. Revista ALCONPAT, 5(2), pp. 151-161, 2015. DOI: 10.21041/ra.v5i2.84 [ Links ]

[23] Kocáb, D., Misák, P. and Cikrle, P., Characteristic curve and its use in determining the compressive strength of concrete by the rebound hammer test. Materials, 12(17), 2705, 2019. DOI: 10.3390/ma12172705 [ Links ]

[24] American Association of State Highway and Transportation Officials - AASHTO. Manual for Bridge Evaluation. AASHTO Publications, Washington D.C., United States, 2011, 820 P. [ Links ]

[25] Google Earth. Version 9. Cochabamba, Bolivia, [online]. 2017. Available at: https://earth.google.com/webLinks ]

[26] Climate. Villa Tunari, Cochabamba, Bolivia, [online]. 2020. Available at: https://es.climate-data.org/america-del-sur/bolivia/cochabamba/villa-tunari-481118Links ]

[27] UNI. Italian Standard 7928: Determination of Chloride Ion Penetration. UNI, Rome, Italy, 1978. [ Links ]

[28] RILEM Recommendations. CPC-18 Measurement of hardened concrete carbonation depth. Materials and Structures, 21, pp. 453-455, 1988. DOI: 10.1007/BF02472327 [ Links ]

[29] Associação Brasileira de Normas Técnicas - ABNT. NBR 7584: Concreto endurecido - avaliação da dureza superficial pelo esclerômetro de reflexão, ABNT, Rio de Janeiro, Brasil, 1995. [ Links ]

[30] Tuutti, K., Corrosion of steel in concrete. Sweden: CBI, 1982. 468 P. [ Links ]

[31] Lima, M.G., Ações do meio ambiente sobre as estruturas de concreto, en: Isaia, G.C., Concreto, Ciência e Tecnologia. Ibracon, São Paulo, Brazil, 2011, pp. 733-772. [ Links ]

[32] Meira, G.R., Andrade, C., Padaratz, I.J., Alonso, C. and Borba, J.C., Chloride penetration into concrete structures in the marine atmosphere zone - Relationship between deposition of chlorides on the wet candle and chlorides accumulated into concrete. Cement and Concrete Composites, 29(9), pp. 667-676, 2007. DOI: 10.1016/j.cemconcomp.2007.05.009 [ Links ]

[33] Malheiro, R., Meira, G., Lima, M. and Perazzo, N., Influence of mortar rendering on chloride penetration into concrete structures. Cement and Concrete Composites, 33(2), pp. 233-239, 2011. DOI: 10.1016/j.cemconcomp.2010.11.003 [ Links ]

[34] Kim, M.-Y., Yang, E.-I. and Yi, S.-T., Application of the colorimetric method to chloride diffusion evaluation in concrete structures. Construction and Building Materials, 41, pp. 239-245, 2013. DOI: 10.1016/j.conbuildmat.2012.11.084 [ Links ]

[35] Breysse, D., Nondestructive evaluation of concrete strength: an historical review and a new perspective by combining NDT methods. Construction and Building Materials, 33, pp. 139-163, 2012. DOI: 10.1016/j.conbuildmat.2011.12.103 [ Links ]

[36] Proceq. Manual de operación - Martillo para ensayos de hormigón N/L. Proceq, Suiza, 2017. [ Links ]

[37] Instituto Boliviano de Normalización y Calidad - IBNORCA. Norma Boliviana CBH 87: Hormigón Armado. Bolivia, IBNORCA, La Paz, Bolivia, 1987. [ Links ]

[38] Figueiredo, E.P. ando Meira, G., Boletim Técnico 6: corrosão das armaduras das estruturas de concreto. Alconpat, Mérida, México, 2013. [ Links ]

[39] Rocha, J.H.A., Póvoas, Y.V. and Santos, C.F., Detection of delaminations in sunlight-unexposed concrete elements of bridges using infrared thermography. Journal of Nondestructive Evaluation, 38(8), 2019. DOI: 10.1007/s10921-018-0546-5 [ Links ]

[40] Chen, S., Laefer, D.F., Mangina, E., Zolanvari, S.M.I. and Byrne, J., UAV Bridge inspection through evaluated 3D reconstructions. Journal of Bridge Engineering, 24(4), art. 05019001, 2019. DOI: 10.1061/(ASCE)BE.1943-5592.0001343 [ Links ]

J.H.A. Rocha, received the BSc. Eng in Civil Engineering in 2011 from the Universidad Mayor de San Simón, Cochabamba, Bolivia. He obtained the MSc. degree in Civil Engineering in 2018 from the Universidade de Pernambuco, Recife, Brasil. From 2012 to 2017, he worked for construction and consulting companies; and since 2018, for the Universidad Privada del Valle. Currently, he is a Professor in the Civil Engineering Department, Facultad de Tecnología, at the Universidad Privada del Valle. His research interests include bridge inspection, nondestructive testing, concrete technologies and building materials.ORCID: 0000-0002-3383-6379

R. Ibarra-Villanueva, received the BSc. Eng in Civil Engineering in 2011 from the Escuela Militar de Ingeniería. Currently, he is a MSc. student at the Universidad Privada Boliviana. He worked in programs and projects of the construction area. Since 2013, he worked at the Empresa Nacional de Electricidad, Bolivia.ORCID: 0000-0002-0294-8810

How to cite: How to cite: Rocha, J.H.A. and Ibarra-Villanueva, R. Identification and analysis of pathological defect appearance in superstructures of reinforced-concrete bridges in Chapare region, Bolivia. DYNA, 88(216), pp. 15-21, January - March, 2021

Received: June 12, 2020; Revised: November 19, 2020; Accepted: November 27, 2020

Creative Commons License The author; licensee Universidad Nacional de Colombia