SANABRIA-MARTINEZ, Felipe; VALBUENA-NINO, Ely D.; CHACON-VELASCO, Leidy S.  e  ESTUPINAN-DURAN, Hugo A.. Electrochemical Behavior of a Stainless Steel Superficially Modified with Nitrogen by Three-dimensional Ion Implantation. Ing. Investig. [online]. 2022, vol.42, n.1, e106.  Epub 22-Out-2021. ISSN 0120-5609.  https://doi.org/10.15446/ing.investig.v42n1.85772.

Martensitic-grade stainless steels are widely used in diverse industrial and surgical applications, despite their natural tendency to suffer local and uniform corrosion when continuously exposed to aggressive operation conditions. In order to enhance their surface properties, this paper characterized the performance, in saline solutions, of AISI 420 stainless steel, which was surface-modified by three-dimensional ion implantation using electrochemical techniques. The surface of the samples was implanted with ionized nitrogen particles with an energy of 10 keV, varying the implantation time between 30 and 90 minutes. After the surface treatment, the samples were exposed to a NaCl 3% (w/w) aqueous solution for 21 days. Tafel extrapolation, linear polarization resistance, and electrochemical impedance spectroscopy tests were performed, with the purpose of quantifying the effect of the ion implantation technique against electrochemical corrosion. To establish a comparison, the same tests were also performed on non-treated samples. The results indicated an increase in the corrosion potential, polarization resistance, and a decrease in the current density of implanted samples, thus demonstrating that, by delaying corrosive activity, three-dimensional ion implantation offers better protection against electrochemical corrosion in AISI 420 stainless steel samples implanted with nitrogen.

Palavras-chave : martensitic steel; surface; surface modification; corrosion; electrochemical characterization.

        · resumo em Espanhol     · texto em Inglês     · Inglês ( pdf )