FRANCO MEDINA, EDGAR; DELVASTO ARJONA, SILVIO; ZULUAGA CORRALES, FABIO e AMIGO BORRAS, VICENTE. MORPHOLOGICAL AND MECHANICAL RESPONSE CHARACTERIZATION OF NANOFIBER AGGREGATES OF PVA PRODUCED BY ELECTROSPINNING SOL-GEL PROCESS. Dyna rev.fac.nac.minas [online]. 2013, vol.80, n.178, pp.109-114. ISSN 0012-7353.
This work deals with the preparation of poly (vinyl alcohol) solutions composed of a surface active agent, an acid and water. With this solution firstly electrospun nanofiber mats and then nanofiber aggregates were obtained by electrospinning/sol-gel process. The samples were morphologically characterized using scanning electron microscopy (SEM) and Atomic Force Microscopy (AFM), obtaining superficial roughness values, distribution and average diameter before and after the electrospinning/sol-gel process. The PVA nanofiber aggregate reached a maximum strength and a modulus of 90 MPa and 2.55 GPa, respectively. Experimental results show that these fibers have a potential use as secondary reinforcement materials in cementitious composites.
Palavras-chave : Electrospinning; poly (Vinyl Alcohol); nanofiber aggregate; electrospinning/sol-gel process.