SciELO - Scientific Electronic Library Online

 
vol.83 número195Probabilistic seismic hazard analysis using a new ground motion intensity measureSol-gel synthesis of zinc oxide nanoparticle at three different temperatures and its characterization via XRD, IR and EPR índice de autoresíndice de assuntospesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados

Journal

Artigo

Indicadores

Links relacionados

  • Em processo de indexaçãoCitado por Google
  • Não possue artigos similaresSimilares em SciELO
  • Em processo de indexaçãoSimilares em Google

Compartilhar


DYNA

versão impressa ISSN 0012-7353

Resumo

VASQUEZ-MOLINA, Diego; MEJIA-ARCILA, Johanna M.  e  GUTIERREZ, Ruby Mejía-de. Mechanical and thermal performance of a geopolymeric and hybrid material based on fly ash. Dyna rev.fac.nac.minas [online]. 2016, vol.83, n.195, pp.216-223. ISSN 0012-7353.  https://doi.org/10.15446/dyna.v83n195.50824.

This article presents an evaluation of the thermal behavior of a hybrid (FA/OPC) and geopolymer (FA100) material. The FA100 system is based on fly ash (FA), which has an elevated content of unburned material (14.8%). The FA/OPC system is comprised of a mixture of fly ash and ordinary Portland cement (OPC) at a proportion of 80/20. The thermal performance was evaluated by several tests, such as exposure to high temperatures (up to1000°C) and direct flame resistance. In addition, the effect of cyclic exposure was studied at 700°C for 10 cycles. FA/OPC hybrid material retains 92% of its initial strength and FA100 retains 113.3% of its initial strength at 700°C. Both materials can withstand 10 exposure cycles with a strength loss of less than 45%. In direct flame exposure, a temperature gradient of about 500°C was observed. These results indicate that these types of materials could possibly be used as fire-resistant materials in civil structures.

Palavras-chave : fly ash; geopolymer; hybrid material; fire resistance.