vol.85 número207Obtaining minimally processed strawberry (Fragaria x ananassa) products and their physicochemical, microbiological, and sensory characterization by using edible coatingsArtificial pancreas: glycemic control strategies for avoiding hypoglycemia índice de autoresíndice de assuntospesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados

Artigo

Indicadores

Links relacionados

  • Em processo de indexaçãoCitado por Google
  • Não possue artigos similaresSimilares em SciELO
  • Em processo de indexaçãoSimilares em Google

Compartilhar


DYNA

versão impressa ISSN 0012-7353

Resumo

BORJA-GOYENECHE, Estrella Natali  e  OLAYA-FLOREZ, Jhon Jairo. A microstructural and corrosion resistance study of (Zr, Si, Ti)N-Ni coatings produced through co-sputtering. Dyna rev.fac.nac.minas [online]. 2018, vol.85, n.207, pp.192-197. ISSN 0012-7353.  http://dx.doi.org/10.15446/dyna.v85n207.73304.

This work researches the influence of the nickel content on the structural and anticorrosive properties of ZrSiTiN films deposited by means of reactive co-sputtering on alloys of Ti6Al4V. The morphology and structure were analyzed by means of scanning electron microscopy (SEM) and X-ray diffraction (XRD), and the chemical composition was identified via X-ray scattering spectroscopy (EDS). The corrosion resistance was studied using potentiodynamic polarization (PP) tests employing a 3.5% by weight NaCl solution. In the films, an increase of Ni up to 6.97 at% was observed, while in XRD the FCC phase of (Zr, Ti) N was identified, with a mixed orientation in planes (111) and (200), which tended to diminish with the increase of Ni. Finally, with the addition of Ni, the corrosion current densities were reduced from 5.56 x 10-8 to 2.64 x 10-9 A/cm 2. The improvement in the corrosion resistance is due to the effect of the Ni on the microstructure of the system (Zr, Ti) N, which can improve the quality of the passive film and prevent crystalline defects and corrosion zones.

Palavras-chave : sputtering; thin films; corrosive; nickel.