SciELO - Scientific Electronic Library Online

 
vol.87 número213Evaluación de calidad de potencia de la interconexión de una micro red a un sistema de distribución local utilizando simulación en tiempo realDiseño factorial de concretos de polvos reactivos conteniendo escoria de arco eléctrico y polvo de vidrio reciclado índice de autoresíndice de materiabúsqueda de artículos
Home Pagelista alfabética de revistas  

Servicios Personalizados

Revista

Articulo

Indicadores

Links relacionados

  • En proceso de indezaciónCitado por Google
  • No hay articulos similaresSimilares en SciELO
  • En proceso de indezaciónSimilares en Google

Compartir


DYNA

versión impresa ISSN 0012-7353versión On-line ISSN 2346-2183

Resumen

GARCIA-LEON, Ricardo Andrés; MARTINEZ-TRINIDAD, José; CAMPOS-SILVA, Iván  y  WONG-ANGEL, Wilbert. Mechanical characterization of the AISI 316L alloy exposed to boriding process. Dyna rev.fac.nac.minas [online]. 2020, vol.87, n.213, pp.34-41. ISSN 0012-7353.  https://doi.org/10.15446/dyna.v87n213.82924.

In this study, the powder-pack boriding process on low-carbon stainless steel was carried out at 1273 K for 4 h of exposure to obtain a layer around ~57 μm conformed by FeB, Fe2B, and others alloying elements. Firstly, the presence of iron borides formed on the surface of borided AISI 316L alloy was confirmed by optical microscopy combined with the X-ray diffraction analysis. After, the sensed Vickers indentation test was performed on the iron boride layer to estimate the behavior of hardness and Young’s modulus. Sliding wear tests on the borided AISI 316L alloy were performed according to the ASTM G133-05 standard procedure, with the following conditions: distances of 50 and 150 m, normal loads of 5 and 20 N, and a sliding speed of 30 mm/s. Finally, the results showed that the presence of FeB-Fe2B improves the resistance to wear around 41 times compared to the untreated material.

Palabras clave : Boron; stainless steel; hardness; diffusion; residual stresses.