GONZALEZ VERA, Oscar Fernando; MUTIZ, Jhon Jairo  and  URRESTA ARAGON, Julián. Synthesis and characterization of Cu type catalysts supported on MgO, SiO ₂ , ZnO, and Al ₂ O ₃ applied to the hydrogenolysis of glycerol. Rev. ion [online]. 2017, vol.30, n.2, pp.31-41. ISSN 0120-100X.  https://doi.org/10.18273/revion.v30n2-2017003.

In this study the conversion of glycerol to 1,2-propanediol using Cu/MgO, Cu/SiO2, Cu/ZnO and Cu/ Al2O3 catalysts with 10 and 20% Cu contents were evaluated. The copper catalysts were obtained by the incipient wet impregnation method (IWI), using as a precursor a 1M trihydrate copper (II) nitrate solution. The characterization of the catalysts was carried out by the techniques of infrared spectroscopy, solving the characteristic signals at 1633cm-1 and 1383cm-1 indicating the presence of nitrates, whereas by X-ray diffraction it is possible to show the corresponding characteristic peaks to the planes of the tenorite (1 1 -1) and (1 1 1), at the 2θ angles of 35.6 ° and 38.7 ° respectively, indicating that the tenorite CuO is present in all solid systems in this study and that is the tenorite the active phase for transformation of glycerol. On the other hand, transmission electron microscopy (TEM) allowed to confirm the presence of particles with sizes varying between 100 and 800 nanometers depending on the support. This study demonstrates that the conversion of 84% glycerol and the selectivity towards the 1,2-propanediol around 52% is favored when using the catalyst based on Cu20%/MgO activated at 573K at the reaction conditions of 473K and 20bar, whereas when this same catalyst is activated at 623K under the same reaction conditions, the selectivity is increased to 63% with a decrease in conversion to 65% which in comparison with the other catalytic systems shows that this Cu20%/MgO is the best catalyst in this study.

Keywords : glycerol; hydrogenolysis; 1,2-propanediol; Cu catalyst; incipient wet.

        · abstract in Spanish | Portuguese     · text in Spanish     · Spanish ( pdf )