SciELO - Scientific Electronic Library Online

 
 issue43Production and characterization of porous bodies of synthetic hydroxyapatiteHydration process in ordinary portland cement paste with thermally treated kaolin author indexsubject indexarticles search
Home Pagealphabetic serial listing  

Services on Demand

Journal

Article

Indicators

Related links

  • On index processCited by Google
  • Have no similar articlesSimilars in SciELO
  • On index processSimilars in Google

Share


Revista Facultad de Ingeniería Universidad de Antioquia

Print version ISSN 0120-6230On-line version ISSN 2422-2844

Abstract

MARIN PAREJA, Nathalia; ESCOBAR, Diana Marcela; OSSA, Claudia Patricia  and  ECHAVARRIA, Alejandro. Synthesis and characterization of microporous hydroxyapatite, comparison with a commercial product. Rev.fac.ing.univ. Antioquia [online]. 2008, n.43, pp.67-76. ISSN 0120-6230.

The hydroxyapatite is the natural component of the human bone which can synthetically obtained by the reaction between calcium nitrate and ammonium phosphate keeping its bioactivity properties. Therefore, it can be chemically linked with the bone tissue. In this work microporous hydroxyapatite was obtained by a precipitation method, a polymer was added to generate the porosity and calcined at 750 and 850 °C. The synthesized hydroxyapatite (denominated HA UdeA) was compared with a commercial product. The samples were characterized by X Ray Diffraction (XRD), Fourier Transformed Infra Red (FTIR), Scanning Electronic Microscopy (SEM) and Thermoanalytical techniques (DTA - TGA). The results indicate that HA UdeA and the commercial product presented similar characteristics as crystalline structure, chemical composition and adsorption of species. Although some differences in shape and particle size were observed both ceramics can be used as implant biomaterials, for example in bone repair.

Keywords : hydroxyapatite; porosity; bone repair; calcium phosphate; oseointregration.