PEREZ MUNOZ, Diego; MARULANDA-AREVALO, José Luddey  e  MORENO-TELLEZ, Carlos Mauricio. Corrosion protection in saline environment of a carbon steel coated (aluminum & three-layer painting system) by eats. Rev.fac.ing.univ. Antioquia [online]. 2018, n.89, pp.26-33. ISSN 0120-6230.  https://doi.org/10.17533/udea.redin.n89a04.

This paper presents a comparative study on corrosion protection of low-carbon steel coated with two different painting systems. The first set of samples was coated with an aluminum layer of primer deposited by Electric Arc Thermal Spray (EATS), after which two additional layers of paint were applied, thereby creating an aluminum-painting system; while the second set of samples was coated with the traditional three-layer painting system (zinc-rich layer of primer). Afterwards, all the samples were exposed to the salt spray chamber. The samples were monitored to record their reactions in the corrosive saline environment. Scanning Electron Microscopy (SEM), adhesion and electrochemical corrosion tests were performed to characterize the coatings and report changes in their properties (adhesion, topography and homogeneity), which are related to exposure time. The three-layer painting system barely complied with manufacturer claims on protection time under corrosive conditions; on the other hand, the aluminum-painting system yielded better results by prolonging protection time.

Palavras-chave : Aluminum; Corrosion; EATS; Paint; Saline environment.

        · resumo em Espanhol     · texto em Inglês     · Inglês ( pdf )