RODRIGUEZ-CASTRO, Leidys Marleyn; URBIZTONDO-CASTRO, Miguel e PINA-IRITIA, Maria Pilar. Influence of boehmite intermediate layer as covalent linker on synthesis of LTA zeolite coatings. Rev.fac.ing.univ. Antioquia [online]. 2021, n.101, pp.64-73. Epub 16-Set-2021. ISSN 0120-6230. https://doi.org/10.17533/udea.redin.20200693.
The incorporation of nanostructured materials, such as LTA-type zeolite on the silicon wafers, opens a very interesting door to the use of these materials within silicon based microfabrication technologies. This work studies the deposition and intergrowth of defect-free LTA-type zeolite layer onto 3-inch Silicon wafers with a layer of SiO2 subjected to pretreatment. The main disadvantage associated with zeolite layer synthesis are crack the formation of cracks and difficulty of obtaining a uniform layer. By modifying the supports with boehmite, a substantial improvement was observed in terms of layer continuity and crystal intergrowth in comparrison to coatings prepared on cationic polymer, poly (diallyldimethylammonium chloride). An LTA- type zeolite layer was synthesized in a range of 350 to 1300 nm via hydrothermal ex-situ method at 363 K for 12 h. Tetramethylammonium hydroxide (TMAOH) was used as a template, and aluminum isopropoxide and colloidal silica were used as Al and Si sources, respectively.
Palavras-chave : Coating; zeolite; hydrothermal synthesis; boehmite; silicon support.