SciELO - Scientific Electronic Library Online

 
vol.22 número34Sputtering in Abnormal Glow Discharge at 800°C of TemperatureSolid Waste Management Evaluation at the Universidad Pontificia Bolivariana, Bucaramanga's Campus índice de autoresíndice de assuntospesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados

Journal

Artigo

Indicadores

Links relacionados

  • Em processo de indexaçãoCitado por Google
  • Não possue artigos similaresSimilares em SciELO
  • Em processo de indexaçãoSimilares em Google

Compartilhar


Revista Facultad de Ingeniería

versão impressa ISSN 0121-1129

Resumo

MARULANDA AREVALO, José Luddey; PEREZ TRUJILLO, Francisco Javier  e  REMOLINA MILLAN, Aduljay. Aluminum-Silicon Coatings Made by Chemical Vapor Deposition in Fluidized Bed on Stainless Steel AISI 316. Rev. Fac. ing. [online]. 2013, vol.22, n.34, pp.63-70. ISSN 0121-1129.

The aluminum-silicon coatings were deposited on stainless steel AISI 316, by chemical vapor deposition, in fluidized bed reactors (CVDFBR), in the 540 to 560°C temperature range, using a bed formed by a 2.5 g silicon and 7.5 g aluminum powder and 90 g inert bed (alumina), which was fluidized with Ar. As activators were used a mixture of HCl/H2 in ratios of 1/10 to 1/16. Furthermore, the coatings deposition time was varied between 45 minutes to 1.5 hours, with a volume ratio of 50% active gases, and 50% neutral gases. A thermodynamic simulation was conducted with the software Thermocalc for information about the possible composition and the amount of material deposited, for the selected conditions. Among the coatings are FeAl2Si, FeAl2 and Fe2Al5. Aluminum-silicon coatings were heat treated to improve their mechanical properties and behavior against oxidation. The inter diffusion of the alloying elements and the heat treatment causes the aluminum to diffuse into the substrate and the iron diffuse into the coating surface, achieving the above compounds transformation in FeAl, Al2FeSi, Cr3Si, and AlFeNi AlCrFe.

Palavras-chave : Aluminum-Silicon Coating; Chemical Vapor Deposition; Stainless Steel; Intermetallic; Fluidized bed.