SciELO - Scientific Electronic Library Online

 
 número16ANÁLISE DO DESEMPENHO DE PLANTAS DE GESTÃO DE RESÍDUOS SÓLIDOS NO NORTE DO VALLE DEL CAUCA, COLÔMBIASWAPS DE TAXA DE INTERESSE E DE CRUZE DE MOEDAS COMO FERAMENTAS DE COBERTURA PARA AS EMPRESAS COLOMBIANAS índice de autoresíndice de assuntospesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados

Artigo

Indicadores

Links relacionados

  • Em processo de indexaçãoCitado por Google
  • Não possue artigos similaresSimilares em SciELO
  • Em processo de indexaçãoSimilares em Google

Compartilhar


Revista EIA

versão impressa ISSN 1794-1237
versão On-line ISSN 2463-0950

Resumo

RONDON, Hugo Alexánder. BEHAVIOR EVALUATION OF CLAYS SUBJECTED TO DIFFERENT EXPOSURES TIMES AT HIGH TEMPERATURES. Rev.EIA.Esc.Ing.Antioq [online]. 2011, n.16, pp.175-187. ISSN 1794-1237.

Laboratory tests were performed in order to evaluate the effects on the index properties, volumetric behavior and monotonic uniaxial strength of two clays caused by the application of different temperatures (150, 225 and 300 °C) for varying periods of time (1, 7 and 15 days). Additionally, we studied whether the clays recover the mentioned properties after being subjected to high temperatures and being again exposed to room temperature for one week in the laboratory. The mean objective of this research project is to evaluate whether the application of increasing temperatures in clays can be a good stabilization method in the future or if it is possible to produce mineral filler. Results show that the plasticity, expansion potential and monotonic uniaxial strength decrease when the temperature is raised up 150-300 °C on the samples and when the exposure time increased. Additionally, it is reported that the recovery of clay properties is zero when they are subjected to 300 °C for 15 days.

Palavras-chave : temperature; expansive clays; stabilization; index properties.