SciELO - Scientific Electronic Library Online

 
vol.13 número24Renewable Insulation Materials Constructed from Colombian Materials According to the Principles of Sustainable Development: a ReviewBifurcation in the Tidal Streams of Sagittarius: Numerical Simulations índice de autoresíndice de assuntospesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados

Journal

Artigo

Indicadores

Links relacionados

  • Em processo de indexaçãoCitado por Google
  • Não possue artigos similaresSimilares em SciELO
  • Em processo de indexaçãoSimilares em Google

Compartilhar


Tecciencia

versão impressa ISSN 1909-3667

Resumo

CIFUENTES AYA, Hector  e  OLAYA, Jhon Jairo. Anticorrosive Properties of Chromium Coatings on AISI H13 Steel Produced via Gaseous Nitriding in a Vacuum. Tecciencia [online]. 2018, vol.13, n.24, pp.43-52. ISSN 1909-3667.  https://doi.org/10.18180/tecciencia.2018.24.5.

This paper shows the results of this process through the performance of a duplex treatment that combines the application a single chromium hard coating Cr(VI) on a AISI H13 steel with a thermochemical treatment of vacuum gas nitriding. The thickness of the electroplated coating was 15 Lim, and N2 was used as precursor gas, with a flow of 100 ml/min at a pressure of 1.2 kPa to produce a CrxNy coating. The existing phases were determined by means of X-ray diffraction, and the corrosion resistance was evaluated via potentiodynamic polarization and electrochemical impedance spectroscopy techniques in a three-electrode electrochemical cell. Characterization via XRD determined the presence of chromium nitrides of type Cr2N, with an important orientation along the plane (300) associated with the partial pressure of N2 and the thermodynamic behavior. The corrosion resistance results showed a significant decrease in the corrosion current density compared with those exhibited by samples chromed by electroplating with AISI H13 steel without nitriding. These results, coupled with the sealing of characteristic microcracks of the electroplated chrome coating, could improve the corrosion resistance, because of the existence of the CrxNy phase.

Palavras-chave : Chromium Nitrides; Corrosion Resistance; Duplex Treatments; Electroplated Chromium; Vacuum.