SciELO - Scientific Electronic Library Online

 
 número87Latency analysis on W-band hybrid fiber-wireless link using software defined radio in real timeMulti-objective optimization in biotechnological processes: application to plant cell suspension cultures of Thevetia peruviana índice de autoresíndice de assuntospesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados

Journal

Artigo

Indicadores

Links relacionados

  • Em processo de indexaçãoCitado por Google
  • Não possue artigos similaresSimilares em SciELO
  • Em processo de indexaçãoSimilares em Google

Compartilhar


Revista Facultad de Ingeniería Universidad de Antioquia

versão impressa ISSN 0120-6230

Rev.fac.ing.univ. Antioquia  no.87 Medellín abr./jun. 2018

https://doi.org/10.17533/udea.redin.n87a04 

Artículo original

Clay surface characteristics using atomic force microscopy

Características superficiales de la arcilla utilizando microscopía de fuerza atómica

Ricardo Andrés García-León1  * 

Eder Norberto Flórez-Solano1 

Carlos Humberto Acevedo-Peñaloza2 

1Grupo de Investigación INGAP, Departamento de Ingeniería Mecánica, Universidad Francisco de Paula Santander. Vía Acolsure, Sede el Algodonal. C. P. 546552. Ocaña, Colombia.

2Grupo de Investigación GIDIMA, Departamento de Ingeniería Mecánica, Universidad Francisco de Paula Santander. Avenida Gran Colombia 12E-96 Barrio Colsag. C. P. 540003. Cúcuta, Colombia.


ABSTRACT

The first component for the manufacture of masonry products used in construction is clay, which provides the plasticity that facilitates the molding and handling of the product. The second component is the feldspar in form of alumina ( Al2O3 ) which is used as flux. The third one is silica ( SiO2 ) which is used as a filling material and stabilizer. These elements are determined by chemical composition using fluorescence analysis or X-ray diffraction, which is the basis of the modern classification of minerals. Thereby, the main objective of this research is to study the surface characteristics of clay samples from an industrial company producing H-10 blocks in the region of Norte de Santander, by studying the surfaces of the samples selected through the analysis by Atomic Force Microscopy, in order to compare the results with those found in the literature, and at the same time taking into account the chemical elements in their highest composition. The results show that this is a technique that allows the identification of clay components, thus validating what has been found in physical and chemical analysis, expecting to provide a scientific contribution by AFM, because there is little information related to the characterization topography of clay materials.

Keywords: Clays; masonry; FRX; DRX; AFM

RESUMEN

El primer componente para la fabricación de productos de mampostería para la construcción es la arcilla, la cual aporta la plasticidad que facilita el moldeo y el manejo del producto. El segundo componente es el feldespato en su formación como alúmina ( Al2O3 ) que se utiliza como fundente. La tercera es la sílice ( SiO2 ) que se utiliza como un material de relleno y estabilizador. Estos elementos se determinan mediante la composición química por análisis de fluorescencia o difracción de rayos X, la cual es la base de la clasificación moderna de los minerales. De esta manera, el principal objetivo de este trabajo es estudiar las características superficiales de muestras de arcilla de una empresa dedicada a producción de bloques H-10 en la región Norte Santandereana, mediante el estudio de las superficies de las muestras seleccionadas a través de la técnica de Microscopía de Fuerza Atómica con el propósito de comparar los resultados con los obtenidos en la bibliografía teniendo en cuenta los elementos químicos en su mayor composición. Los resultados demuestran que ésta es una técnica que permite identificar los componentes de la arcilla validando de esta manera lo encontrado en los análisis físicos y químicos, con lo cual se espera brindar un aporte científico por AFM o MFA, debido a que existe poca información relacionada en la caracterización topográfica de materiales arcillosos.

Palabras clave: Arcillas; mampostería; FRX; DRX; AFM

1. Introduction

Atomic Force Microscope (AFM) is a mechano-optical instrument capable of detecting forces of the order of nanonewtons. The probe is coupled to a very flexible microscopic bar of only about 200μm Figure 1. The Atomic Force Microscope has been essential in the development of nanotechnology for the characterization and visualization of samples with nanometric dimensions, that is, 10-9 m = 1nm. It is a non-destructive technique of surface measurement based on the interaction of a tip in a pyramidal or conical shape with the surface of the sample that, when traced, is capable of continuously recording the surface. This technique allows the surface analysis of samples with nanometric or even atomic resolution. As a main advantage, it has the possibility of developing measurements without any previous treatment of the sample, and without the need to use vacuum [1,2].

The analysis through this method is characterized by the distribution of amplitudes across an electromagnetic wave phenomenon that is generated, that can be superposition waves of several frequencies. Mathematically, this spectral analysis is related to a tool called a Fourier transform.

The results provide the geometric information from surface images (shape and dimensions) of deposits such as nanoparticles, deposited surface roughness [3,4], Figure 1 shows the operation of the equipment.

Figure 1 Operation of the equipment [5,6]  

The superficial characteristics of the minerals concentrated in the clay in high percentages are presented in the Table 1, according to investigations carried out by several authors.

Table 1 Surface of different compounds 

The uses of such technique make it possible to obtain information about the shape, morphology and size of the clay particles. There are several studies in the literature that studied the characterization of surfaces in atomic scale through AFM, as river humic substances and minerals such as illite and smectite, kaolinite, gibbsite, montmorillonite and goethite. However, the number of studies aiming to characterize the soil clay fraction minerals using this technique is still very low [20-22].

AFM can be used to measure properties of minerals such as clay and to identify the presence of clay minerals, hydrated aluminosilicates. Using this technique, the first quantitative measurements of the Young's Clay module are presented. For example, the Young's modulus of dickite according to research conducted by Prasad is 6.2 GPa [19].

According to Bastos of Sousa, AFM has been recognized as one of the most powerful tools for analyzing surface morphologies because it creates three-dimensional images on the angstrom and nano scale. This technique has been ideal in the dispersion analysis of nanometric components in nanocomposites and in polymer blends due to the ease of sample preparation and low equipment maintenance cost when compared to scanning electron microscopy [23].

Clay minerals are playing an increasingly important role in nanocomposites for the remarkable property improvements in comparison with the normal microscopic counterparts, such as nanometer thickness, extraordinary high surface area and ease, properties allowing hybridization by polymers or ions to form new composites [24]. However, in the mineralogy properties, lattice defects such as isomorphous substitution present in the clay or nanosheet surface are known to significantly affect clay property. Generally, clay minerals are composed of silica tetrahedron (T) and alumina or magnesia octahedral sheet (O) and form the T-O-T layer structure or the T-O layer structure [25].

Likewise, reliable techniques to measure both particle size and shape distributions are required to gain a better understanding of the impact of particle size and shape, and select the most appropriate pigments for obtaining a coating with specific end-use properties. Moreover, there are several commercial instruments for determining particle size in the near-micron range [26].

In the research carried out by Schoonheydt, they developed an AFM analysis to study clay mineral films and clay-based catalysts based on the mechanical properties and the number of layers formed in each particle, identifying mainly sizes and shapes of the particles with a homogeneous distribution of the surface [27].

Most of the research conducted on this topic describes the contributions that AFM uses, with emphasis on the dispersion of nanofilters in matrix polymers, besides showing the importance of technical analysis for nanocomposites and mixtures of polymers based on elastomers.

The quantitative characterization techniques used for conventional composites include microstructure image analysis from which a number of quantitative measures, whether deterministic or probabilistic, are calculated. Deterministic measures include quantities such as intercept lengths. Therefore, it is possible to modify and update the quantitative characterization techniques used for conventional compounds to extend their use for nanocomposites.

2. Materials and methods

In the present study, it was used the laboratory equipment Veeco Multimode V Model Atomic Force Microscope made in the United States, using the Nanoscope 7.3 Software to analyze and measure the images obtained, in order to study the surfaces or topography of the samples in contact mode with a sharp tip that perceives the force emitted by the surface according to the type of material. This equipment has modules for magnetic tests, in fluids and tunneling at room temperature, in addition to a scanner that can control the temperature of the samples in a range from -35 to 250°C. The obtaining geometric information was derived from topographic images (shape and dimensions) of deposits such as nanoparticles and surface roughness.

This analysis was developed in the laboratories of the National Polytechnic Institute in Mexico, using a mechano-optical instrument capable of detecting forces of the order of nanonewtons, shown in Figure 2.

Figure 2 Atomic Force Microscope 

Five samples of clay of the raw material lot of a company dedicated to the manufacture of masonry products for construction were selected. Also, it is important to mention that the analyses performed are to validate an alternative characterization of ceramic materials and thus predict the behavior in the transformation phases of the material in the production process. In addition, the main objective was to study the presence of aluminosilicates (Al 2 O 3, SiO 2, K 2 O, among others) that are the elements present mostly in this type of materials; approximately 50 images were obtained but the most relevant ones were selected.

The results were validated with X-ray fluorescence analysis, the preparation of the samples for analysis consisted of the crushing according to ASTM C323-56, screening the material for 400 mesh, until obtaining a particle size of 38 μm, (If the particle size of the sample is greater than 63 microns); Six grams of the original sample are taken to a hydraulic press at 15 tons for 1 minute, thus obtaining a pellet of 30 mm diameter for analysis in the Bruker S4 Explorer fluorescence equipment with Detector Pro4 and X-ray tube Rh at a voltage of 40KV and 25mA [28-31].

The samples of clay were then subjected to the calcination process, which consists of carrying each sample at 1000°C and maintaining it at that temperature for 1 hour, to evaluate the weight percentage lost during the treatment after weighing the sample before and after, at 105°C. These calcination losses L.O.I. (Loss On Ignition) represent the amount of volatile components (H 2 O, CO 2, F, Cl y S) and organic matter not detected with the fluorescence equipment.

For the success of laboratory tests, samples were taken randomly taking into account that they were too small without the need to perform any type of preparation. In the present study, AFM technique was employed to characterize the morphology and microtopography of the main minerals present in the clay fraction from the superficial layer of a soil in the industries dedicated to the fabrication of masonry products in Ocaña Norte de Santander. In the characterization, image analysis programs, XRF spectroscopic techniques and XRD were used together to determine and quantify the main minerals identified [32].

3. Results and discussion

The surface images were taken at 5 µm for 5 µm and in some with a 2 µm for 2 µm approach for each particle of clay mineral samples, with the help of software which has the equipment to identify the structures present in the samples by means of the frequency distributions obtained.

3.1 AFM results

Taking into account the above and the selected samples, the following results were obtained for the surfaces of the samples selected in 2 and 3 dimensions, as well as the distribution of frequencies to the grouping of data that analyzes the equipment in mutually exclusive conditions which indicate the number of observations in each category, with respect to the areas of the surfaces, being a characteristic graph for each element of the sample obtained from the computer software. This provided an added value to the grouping of data as shown in the following figures from 3 to 12 as in all AFM images, topographic differences are originally color coded and then converted to a scale where red are immersions and yellow are the maximum. Because of the above, images taken on the microscope of force atomic are shown in Figure 3.

Figure 3 Topography for the sample 1. (a) 3D top view. (b) 2D view. (c) 3D view 

The topographic pattern of sample 1 Figure 3 suggests that it contains AlSiO₅(OH)₄ (Caolinite), for which the characteristic frequency graph is shown in Figure 4.

Figure 4 Graph representation of frequency distributions emitted for sample 1 

The previous histogram shows Caolinite has higher depths between 0 to 40 and 350 to 390 mV of 2% surface response.

Figure 5 shows the images taken on the microscope for sample 2.

Figure 5 Topography for the sample 2. (a) 3D top view. (b) 2D view. (c) 3D view 

The topographic pattern of sample 2 Figure 5 suggests that it contains KO 2 (potassium oxide), for which the characteristic frequency graph is shown in Figure 6.

Figure 6 Graph representation of frequency distributions emitted for sample 2 

The previous histogram Figure 6 shows potassium oxide has higher depths between 330 to 380 mV of 4% surface response.

Figure 7 shows the images taken on the microscope for sample 3.

Figure 7 Topography for the sample 3. (a) 3D top view. (b) 2D view. (c) 3D view 

The topographic pattern of sample 3 Figure 7 suggests that it contains Fe 2 O 3 (iron oxide), for which the characteristic frequency graph is shown in Figure 8.

Figure 8 Graph representation of frequency distributions emitted for sample 3 

The previous histogram shows iron oxide has higher depths between 70 to 78 mV of 4,66% surface response.

Figure 9 shows the images taken on the microscope for sample 4.

Figure 9 Topography for the sample 4. (a) 3D top view. (b) 2D view. (c) 3D view 

The topographic pattern of sample 4 Figure 9 suggests that it contains Al 2 O 3 (Alumina) y SiO 2 (Silica), for which the characteristic frequency graph is shown in Figure 10.

Figure 10 Graph representation of frequency distributions emitted for sample 4 

The previous histogram shows alumina and silica has higher depths between 135 to 145 mV of 4,43% surface response.

Figure 11 shows the images taken on the microscope for sample 5.

Figure 11 Topography for the sample 5. (a) 3D top view. (b) 2D view. (c) 3D view 

The topographic pattern of sample 5 Figure 11 suggests that it contains AlSiO₅(OH)₄ (Caolinite), for which the characteristic frequency graph is shown in Figure 12.

Figure 12 Graph representation of frequency distributions emitted for sample 5 

The previous histogram shows Caolinite has higher depths between 350 to 380 mV of 2,96% surface response, being similar to sample 1.

Afterwards, it was observed the samples behave as layers according to the research done by Sachan, taking into account Samples 1 and 5, where the presence of Caolinite is evidently observed. The frequency distribution for all images represents the area and depth of the particle that was analyzed [33].

The distortion present in sample 5 is due to the contact mode of the AFM equipment with the powder of the sample and the type of mineral texture, in addition to the topographic variations that are color-coded. On the other hand, some air current or sudden movement could influence the glass slide and the plate, taking into account that the assembly of the sample on the plate is by pressure and adhered by a special tape [34].

AFM topographies of clay samples as seen in figures from 3 to 12, are in the form of Caolinite for the grains shaped in the form of rosettes; also, the presence of aluminum-silicates are characteristic of this type of material. In addition, the presence of Alumina, Silica and Iron Oxide is also observed in the samples, because these are presented in the form of flat plates (Silica) and others in spheroidal form (Alumina and Iron Oxide), which is of great importance for the investigation; these forms are typical images with topographic variations below 10 nm [18].

According to the technological review, the presence of Al 2 O 3 (Silica), SiO 2 (Alumina), FeO 2 (iron Oxide) and KO 2 (Potassium Oxide) is the most important and relevant taking into account that approximately 50 images of different particles and samples were selected for research. The potassium and iron oxides exhibit similar histogram behavior, but the intensity of the millivolts (mV) of the response surface varies.

In the research developed by Sachan, it was determined that the AFM method worked quite well for different clay microfabricates, confirming reliability and versatility of the method, assuming the potential application to become a routine tool for the identification, quantification and evaluation of soil micro-manufacturers [33].

Finally, the results in the topography of samples varied depending on the type of clay, this could be evidenced in the images obtained by AFM where, as the sample changes, larger and deeper valleys are formed; thus also the decrease in the thickness of the material can be observed.

3.2 Validation of results

The FRX and DRX tests yielded the following results shown Table 2, for comparing the test in AFM.

Table 2 XRF for the sample 1 

The Table 2 shows a high percentage weight of silica (SiO 2) of 54.743 and 56.582 % for the two mixtures, which causes a rapid drying process in cooking and, a decrease in the contraction. The alumina (Al 2 O 3) is also found in high percentages for the two mixtures of 20.670 and 20.565 %, giving it a resistance to high temperatures and a decrease of breaks in cooking. Although the current industrial use of this clay is for construction and the recommended chemical characteristics are of 50 to 60 % for SiO 2 and of 20 to 30 % for Al 2 O 3, with which evidently the presence of montmorillonite clays is verified because its chemical composition is: SiO 2: 48 - 56%, Al 2 O 3: 11 - 22%, MgO: 0.3 - 0.8%, and the percentages obtained in the analysis of XRF make it suitable for this use. The values of the proportions of iron oxide (Fe 2 O 3) are normal up to 10% percentage. This oxide will give it a red color after burning [35]. The low content of alkaline oxides (sodium and potassium) and alkaline earth oxides (magnesium and calcium) makes it possible for the clay to generate the glassy phase at relatively high temperatures (Higher to 900°C), conferring properties of semirefractariety. The presence of a high content of potassium oxide (K 2 O) of 2.926 and 3.301 % above the other alkali and alkaline-earth oxides, classifies it as an illitic material, the other elements are in low proportions that do not affect the structure of the final product [36]. Taking into account the previous values, the other samples must contain percentages similar to sample 1.

Also, the diffractograms of the sample are shown in Figure 13 and Table 3 indicating the quantitative analysis obtained in the laboratory.

Figure 13 XRD for the sample 

Figure 13 shows the composition of the constituent feldspars of rocks corresponds to a ternary system composed of Quartz (SiO 2), Albite (Na (AlSi 3 O 8)) and Caolinite (Al 2 (Si 2 O 5) (OH)4). The above can be checked with the XRD analysis of the following Table 3.

Table 3 Mineralogical structures of the XRD analysis 

Most of the clay mixtures have a composition, for example: 50% kaolinite + 30% quartz + 20% potassium feldspar [37]. As for the clay minerals, it is observed that the majority of the samples is constituted by the Illite in an important proportion (generally it is the second mineral in importance after the quartz). Additionally, some samples contain smectites but in a proportion similar to kaolinite. In addition, the Table 3 shows the phases present in the specimens selected from the samples. They were performed by comparing the profiles observed with the diffraction profiles reported in the PDF-2 database of the International Center for Diffraction Data (ICDD). Quantitative analysis without amorphous determination [38].

4. Conclusions

The resolution and results of images by AFM is a great tool to determine the topographies of the clay compounds used in the ceramics industry by which it can be verified that the texture of the samples are repeated in random places.

The found topographies of the constituent elements of the clay were validated with the XRD and FRX tests, which was of great importance for the investigation, taking into account that the abundant elements were iron oxide, alumina and silica, components found in the topographic images of AFM. These results make a contribution to the scientific community and future work in this area of nanotechnology.

Most of the samples were found in the form of flat plates in mineralogical compound characteristic of silica and others in spheroidal form, alumina and iron oxide forms, which varies the frequency of the histogram as its percentage of area for each of the samples studied.

Additionally, the potential of the AFM is based on the performance of an analysis to determine the contact angle, the hardness and the roughness of the samples with the material that will be carried out in future investigations. On the other hand, for these small pore sizes, a statistical analysis could be performed to determine, on average, the amplitude of these zones as well as to determine the mechanical strength of the particles.

Taking into account the bibliographic review of the literature, it can be affirmed that in the literature no record of complete characterization of clays at manometric level using AFM was found.

The AFM with the help of the XRD and XRF tests provides a broader view of the distribution in the overall volume of the elements and characteristics of the samples, that can lead to a much more reliable prediction of the properties of the nanocomposites. Some of these characterization techniques, which can produce a large-scale distribution analysis in nanocomposites, directly result in a pictorial image of the distribution (e.g. Confocal Raman Microscopy and Atomic Force Microscopy).

5. Acknowledgment

The authors gratefully acknowledge the Instituto Politecnico Nacional unidad Azcapotzalco and especially PhD Juliana Gutiérrez Paredes by conducting the tests and Erick Lambraño for reviewing the article. In addition, to the research group INGAP of the Universidad Francisco de Paula Santander Ocaña.

References

[1] O. Sahin, S. Magonov, C. Su, C. F. Quate, and O. Solgaard, “An atomic force microscope tip designed to measure time-varying nanomechanical forces,” Nature Nanotechnology, vol. 2, no. 8, pp. 507-514, Jul. 2007. [ Links ]

[2] E. A. López and S. D. Solares, “El microscopio de fuerza atómica: métodos y aplicaciones,” Revista de la Universidad del Valle Guatemala, vol. 28, no. 1, pp. 14-28, 2014. [ Links ]

[3] (2012) Atomic force microscopy. University of Rochester. Accessed Apr. 24, 2017. [Online]. Available: Available: www.optics.rochester.edu/workgroups/cml/opt307/spr12/nilotpal/HTMLfiles/AFM.htmLinks ]

[4] V. Ivanov, J. Chu, V. Stabnikov, and B. Li, “Estrengthening of soft marine clay using bioencapsulation,” Journal Marine Georesources & Geotechnology, vol. 33, no. 4, pp. 320-324, Jan. 2015. [ Links ]

[5] S. Pineda, Z. J. Han, and K. Ostrikov, “Plasma-enabled carbón nanostructures for early diagnosis of neurodegenerative diseases,” Materials, vol. 7, no. 7, pp. 4896-4929, Jun. 2014. [ Links ]

[6] L. Vázquez. Afm (atomic force microscope). [Online]. Available: www.icmm.csic.es/fis/espa/afm.htmlLinks ]

[7] N. S. et al., “Characterization of nanoreinforcement dispersion in inorganic nanocomposites: A review,” Materials , vol. 7, no. 6, pp. 4148-4181, May 2014. [ Links ]

[8] S. E. et al., “Manipulation of the catalyst-support interactions for inducing nanotube forest growth,” J. Appl. Phys., vol. 109, no. 4, pp. 044 303.1-044 303.7, Feb. 2011. [ Links ]

[9] Y. Kobayashi, V. Salgueiriño, and L. M. Liz, “Deposition of silver nanoparticles on silica spheres by pretreatment steps in electroless plating,” Chemistry of Materials , vol. 13, no. 5, pp. 1630-1633, Apr. 2001. [ Links ]

[10] L. B. Monroy, J. J. Olaya, M. Rivera, A. Ortiz, and G. Santana, “Growth study of y-ba-cu-o on buffer layers and different substrates made by ultrasonic spray pyrolysis,” Rev. Latinoam. Metal. y Mater., vol. 32, no. 1, pp. 21-29, Jan. 2012. [ Links ]

[11] K. Kim, B. A. Lee, X. H. Piao, H. J. Chung, and Y. J. Kim, “Surface characteristics and bioactivity of an anodized titanium surface,” J. Periodontal Implant Sci., vol. 43, no. 4, pp. 198-205, Aug. 2012. [ Links ]

[12] X. W. T. et al., “In vitro effect of a corrosive hostile ocular surface on candidate biomaterials for keratoprosthesis skirt,” Br. J. Ophthalmol., vol. 96, pp. 1252-1258, Sep. 2012. [ Links ]

[13] T. Öhlund, J. Örtegren, S. Forsberg, and H. E. Nilsson, “Paper surfaces for metal nanoparticle inkjet printing,” Appl. Surf. Sci., vol. 259, pp. 731-739, Oct. 2012. [ Links ]

[14] P. Henrique, C. Camargo, K. G. Satyanarayana, and F. Wypych,“Nanocomposites: Synthesis, structure, properties and new application opportunities,” Mater. Res., vol. 12, no. 1, pp. 1-39, Jan. 2009. [ Links ]

[15] M. R. Belkhedkar, A. U. Ubale, Y. S. Sakhare, N. Zubair, and M. Musaddique, “Characterization and antibacterial activity of nanocrystalline mn doped fe2o3 thin films grown by successive ionic layer adsorption and reaction method,” J. Assoc. Arab Univ. Basic Appl. Sci, vol. 21, pp. 38-44, Oct. 2016. [ Links ]

[16] P. Lu and Y. L. Hsieh, “Highly pure amorphous silica nano-disks from rice straw,” JPowder Technol., vol. 225, pp. 149-155, Oct. 2012. [ Links ]

[17] D. A. C. Brownson, D. K. Kampouris, and C. E. Banks, “Graphene electrochemistry: Fundamental concepts through to prominent applications,” Chemical Society Reviews, vol. 41, no. 21, pp. 6944-6976, Nov. 2012. [ Links ]

[18] B. R. B. et al. (1999, Dec. 9) Atomic force microscopy study of clay mineral dissolution atomic force. [Online]. Available: https://vtechworks.lib.vt.edu/bitstream/handle/10919/25984/Bickmorebrb_diss.pdf?sequence=3. [ Links ]

[19] M. Prasad, M. Kopycinska, U. Rabe, and W. Arnold, “Measurement of young’s modulus of clay minerals using atomic force acoustic microscopy,” Geophys. Res. Lett., vol. 29, no. 8, pp. 13.1-13.4, Apr. 2002. [ Links ]

[20] V. Gupta, M. A. Hampton, A. V. Nguyen, and J. D. Miller, “Crystal lattice imaging of the silica and alumina faces of kaolinite using atomic force microscopy,” J. Colloid Interface Sci., vol. 352, no. 1, pp. 75-80, Dec. 2010. [ Links ]

[21] R. A. García and R. Bolívar, “Caracterización hidrométrica de las arcillas utilizadas en la fabricación de productos cerámicos en ocaña, norte de santander,” INGE CUC, vol. 13, no. 1, pp. 47-56, 2017. [ Links ]

[22] R. A. García , R. Bolívar , and E. N. Flórez, “Validación de las propiedades físico-mecánicas de bloques h-10 fabricados en ocaña norte de santander y la región,” Ingenio UFPSO, vol. 10, no. 1, pp. 17-26, 2016. [ Links ]

[23] F. D. B. de Sousa and C. H. Scuracchio, “The use of atomic forcé microscopy as an important technique to analyze the dispersion of nanometric fillers and morphology in nanocomposites and polymer blends based on elastomers,” Polímeros, vol. 24, no. 6, pp. 661-672, Nov. 2014. [ Links ]

[24] X. Zhang, H. Yi, Y. Zhao, and S. Song, “Quantitative determination of isomorphous substitutions on clay mineral surfaces through afm imaging: A case of mica,” Colloids Surfaces A Physicochem. Eng. Asp, vol. 533, pp. 55-60, Nov. 2017. [ Links ]

[25] M. Brigatti, E. Galán, and B. K. G. Theng, “Chapter 2 structures and mineralogy of clay minerals,” vol. 1, pp. 19-86, Dec 2006. [ Links ]

[26] V. Gélinas and D. Vidal, “Determination of particle shape distribution of clay using an automated afm image analysis method,” Powder Technol., vol. 203, no. 2, pp. 254-264, Nov. 2010. [ Links ]

[27] R. A. Schoonheydt, “Reflections on the material science of clay minerals,” Appl. Clay Sci., vol. 131, pp. 107-112, Oct. 2015. [ Links ]

[28] M. B. Roquet, “Mineralogía de la pegmatita casa de piedra, grupo pegmatítico villa praga - las lagunas, subgrupo potrerillos, san luis, argentina,” in 11° Congreso de mineralogía y metalogenia, San Luis, Argentina, 2013, pp. 133-138. [ Links ]

[29] S. M. Rozo, J. Sánchez, and J. F. Gelves, “Evaluación de minerales alumino silicatos de norte de santander para fabricar piezas cerámicas de gran formato,” Rev. Fac. Ing., vol. 24, no. 38, pp. 53-61, 2015. [ Links ]

[30] N. J. Perales and M. Barrera, “Análisis estructural por drx de una arcilla natural colombiana modificada por pilarización,” Rev. Invest. Univ. Quindío., vol. 24, no. 1, pp. 100-106, 2013. [ Links ]

[31] E. Ramos, J. J. Guzmán, M. C. Sandoval, and Y. Gallaga,“Caracterización de arcillas del estado de guanajuato y su potencial aplicación en cerámica,” Acta Univ., vol. 12, no. 1, pp. 23-30, 2002. [ Links ]

[32] N. M. P. D. et al., “Morphological characterization of soil clay fraction in nanometric scale,” Powder Technol ., vol. 241, pp. 36-42, Jun. 2013. [ Links ]

[33] A. Sachan, “Use of atomic force microscopy (afm) of microfabric study of cohesive soils,” J. Microsc., vol. 232, no. 3, pp. 422-431, Nov. 2008. [ Links ]

[34] L. F. Vesga, “Equivalent effective stress and compressibility of unsaturated kaolinite clay subjected to drying,” J. Geotech. Geoenvironmental Eng., vol. 134, no. 3, pp. 366-378, Mar. 2008. [ Links ]

[35] C. M. F. Vieira, R. Sánchez, and S. N. Monteiro, “Characteristics of clays and properties of building ceramics in the state of rio de janeiro, Brazil,” Constr. Build. Mater., vol. 22, no. 5, pp. 781-787, May 2008. [ Links ]

[36] J. D. Santos, P. Y. Malagón, and E. M. Cordoba, “Caracterización de arcillas y preparación de pastas cerámicas para la fabricación de tejas y ladrillos en la región de Barichara, Santander,” DYNA, vol. 78, no. 167, pp. 50-58, Jul. 2011. [ Links ]

[37] C. M. Ríos, “Uso de materias primas colombianas para el desarrollo de baldosa cerámicas con alto grado de gresificación,” M.S. thesis, Facultad de Minas Escuela de Ingeniería de Materiales, Universidad Nacional de Colombia, Medellín, Colombia, 2009. [ Links ]

[38] L. C. Illera, “Raw materials for the ceramics industry from norte de santander. i. mineralogical, chemical and physical characterization,” Rev. Fac. Ing. Univ. Antioquia, no. 80, pp. 31-37, Jul. 2016. [ Links ]

Received: October 11, 2017; Accepted: April 10, 2018

* Corresponding author: Ricardo Andrés García León e-mail: ragarcial@ufpso.edu.co

Creative Commons License This is an open-access article distributed under the terms of the Creative Commons Attribution License