RODRIGUEZ PEREZ, Jessica et al. High temperatures oxidation of ASTM A335 P92 steel in an molten salts of K2SO4 - NaCl. Ing. Desarro. [online]. 2016, vol.34, n.1, pp.44-63. ISSN 0122-3461. https://doi.org/10.14482/inde.33.2.6368.
In this research the oxidation of ASTM A335 P92 steel and the effect of 40% K2SO4 - 60% NaCl salt mixture at temperatures of 500°C to 700°C in intervals of 50°C with exposure times of1,3,10, 30,100 and 150 hours were evaluated using the standard standardized by the European Federation of Corrosion. Metallographic analysis and hardness analysis were performed before and after the test to identify the possible structural change; evidence of x-ray diffraction (xrd) and scanning electron microscopy (SEM-EDS) were performed to determine the corrosion products present in the steel. By SEM-EDS analysis it is shown that corrosive species such as Cl~, SO4- do not react with the alloying elements of steel. It was also noted that the oxide layers formed showed stability, and good adhesion which confirms the oxides protection on the metal. The "gained weight by salts deposition" curves showed a parabolic behavior, typical of high temperature materials.
Palabras clave : High temperature oxidation; gravimetry; molten salts; K2SO4-NaCl; ASTM A335 P92 steel.