SciELO - Scientific Electronic Library Online

 
vol.74 número153Pt - BASED ANODE CATALYSTS FOR DIRECT ETHANOL FUEL CELLSDESIGN AND CONSTRUCTION OF A DIGITAL PROTOTYPE TO DIAGNOSE FAULTS IN INDUCTION MOTORS índice de autoresíndice de assuntospesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados

Journal

Artigo

Indicadores

Links relacionados

  • Em processo de indexaçãoCitado por Google
  • Não possue artigos similaresSimilares em SciELO
  • Em processo de indexaçãoSimilares em Google

Compartilhar


DYNA

versão impressa ISSN 0012-7353versão On-line ISSN 2346-2183

Resumo

VELEZ, SANTIAGO et al. EFFECT ANALYSIS OF SOME PARAMETERS IN THE ELECTROFORMING PROCESS OF NIQUEL CYLINDRICAL PART AT MILI SCALE. Dyna rev.fac.nac.minas [online]. 2007, vol.74, n.153, pp.203-213. ISSN 0012-7353.

In this work cylindrical nickel pieces electroformed from an standard Watts bath with direct current in acrylic moulds were characterised. The influence of current density, aspect ratio and flow regime on the piece’s characteristics was evaluated. The characterisation included: external and internal conformation analysis, microstructure and microharness analysis. Pieces with a good superficial finish and adequate acrylic mould reproduction where obtained under all tested conditions. The conformational analysis revealed that the defects were located preferably in the internal part and toward the last third of the growth. The most homogeneous and with less defects pieces were those deposited with current density 10 A dm-2, bath speed 10 mm s-1 and diameter 0.4 mm. Hardness values were located around 250 HV, but values up to 400 HV were observed.

Palavras-chave : Proceso LIGA; electrodepositación; densidad de corriente; relación de aspecto; régimen de flujo.