SciELO - Scientific Electronic Library Online

 
 número41Husk of rice as source of SiO2Jacobsen’s catalyst anchored on Al-MCM-41 and NH2 group modified Si-MCM-41 as heterogeneous enantioselective epoxidation catalyst using in situ generated dimethyldioxirane as oxidant índice de autoresíndice de assuntospesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados

Artigo

Indicadores

Links relacionados

  • Em processo de indexaçãoCitado por Google
  • Não possue artigos similaresSimilares em SciELO
  • Em processo de indexaçãoSimilares em Google

Compartilhar


Revista Facultad de Ingeniería Universidad de Antioquia

versão impressa ISSN 0120-6230
versão On-line ISSN 2357-53280

Resumo

ESCOBAR, Diana Marcela et al. Paintings pigmented with doped magnetite: preliminary evaluation of anticorrosive properties. Rev.fac.ing.univ. Antioquia [online]. 2007, n.41, pp.21-30. ISSN 0120-6230.

Pure magnetite and magnetite doped with three different concentrations of chromium and copper was lab synthesized. The relative performance of these products as anticorrosive pigments is compared with commercially available hematite (red iron oxide). Special mixtures of the pigments with a solventless epoxy binder were prepared maintaining the pigment volume contents near the practical critical value. The purpose was to distinguish the inhibitive action of pigments with the least possible influence from the barrier properties of the epoxy resin. The performance of mixtures applied on mild steel is characterized in accelerated outdoor exposure, in alternated immersion tests and in total immersion conditions. The latter test was monitored with open circuit potential and impedance measurements. Complementary tests with freestanding films were also performed. The results show that magnetite is not an inert pigment. Therefore presence of doping elements can improve the performance of anticorrosive magnetite paints. Based on this result, a complete formulation with pigment, solvent and additives is suggested and preliminarily tested in the lab aiming at producing an anticorrosive primer.

Palavras-chave : Coatings; paints; impedance; magnetite; copper; chromium; corrosion.