SciELO - Scientific Electronic Library Online

 número55Degradation and adsorption of AZO RR239 dye in aqueous solution by nanoscale zerovalent iron particles immobilized on sawdustHeavy metals in Sinú river, department of Córdoba, Colombia, South America índice de autoresíndice de assuntospesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados



Links relacionados

  • Em processo de indexaçãoCitado por Google
  • Não possue artigos similaresSimilares em SciELO
  • Em processo de indexaçãoSimilares em Google


Revista Facultad de Ingeniería Universidad de Antioquia

versão impressa ISSN 0120-6230
versão On-line ISSN 2422-2844


TROCHEZ, Jenny Johanna; TORRES AGREDO, Janneth  e  MEJIA DE GUTIERREZ, Ruby. Study of hydration of cement pastes added with used catalytic cracking catalyst (FCC) from a colombian refinery. Antioquia [online]. 2010, n.55, pp.26-34. ISSN 0120-6230.

This paper analyzes the effect of the incorporation of industrial waste from an oil refinery in Colombia, known as used catalytic cracking catalyst (FCC), in the hydration process of cementitious pastes. For this purpose, ordinary Portland cement pastes (OPC) added in percentages of 10 and 20% of FCC were prepared. The pozzolanic reactivity of the material and type of hydration products were determined by X-ray diffraction (XRD) and thermogravimetric analysis (TG / DTG). Additionally, the heat of hydration released was determined based on the standard ASTM C186. The results indicate that the hydration process of FCC blended cement is strongly exothermic as a consequence of its pozzolanic activity. The main phases present in the blended cement system were the calcium silicate hydrates (CSH gel), calcium aluminate hydrates (CAH) y calcium aluminosilicate hydrates (CASH), similar to the products obtained in metakaolin blended cement pastes.

Palavras-chave : Catalytic cracking catalyst; blended cement pastes; pozzolanic reactivity; hydration products; heat of hydration.