GOMEZ, MARYORY ASTRID et al. EFEITO DA TEMPERATURA SOBRE A RESISTÊNCIA À TRAÇÃO DE ALGUNS REFORZOS DE FIBRAS PARA MATRIZES CERÁMICAS OU POLIMÉRICAS. Rev.EIA.Esc.Ing.Antioq [online]. 2009, n.11, pp.65-75. ISSN 1794-1237.

Este artigo apresenta um estudo das propriedades termomecánicas de fibras de aço baixo carbono, de aço inoxidável ASI-SAE 304, de aramida e de carbono. Além disso, se analisou o aspecto superficial de reforços de lã mineral de rocha e lã de aluminosilicatos antes e depois que submetê-las a tratamentos térmicos a 1000 ºC. A resistência à tração das fibras se avaliou antes e depois de submetê-las a tratamentos térmicos a temperaturas de 400, 600, 800 e 1000 ºC dependendo da degradação que mostraram. Além disso, se efetuou uma análise termogravim étrica a cada tipo de fibra para determinar as mudanças de peso a diferentes temperaturas. As fibras de aço inoxidável mostraram a maior estabilidade termomecânica, enquanto as fibras de aramida com tratamentos a 400 ºC mostraram propriedades mecânicas praticamente nulas.

Keywords : fibras de aço; fibras cerâmicas; reforços minerais; resistência à tração; tratamento térmico; estabilidade térmica.

        · abstract in English | Spanish     · text in Spanish     · Spanish ( pdf )

 